Análise física, mecânica e de durabilidade do concreto para produção de artefato de meio-fio com agregados naturais e reciclado da cidade de Manaus

Análise física, mecânica e de durabilidade do concreto para produção de artefato de meio-fio com agregados naturais e reciclado da cidade de Manaus

Physical, Mechanical and durability analysis of the concrete to produce curb artifact with natural and recycled aggregates of the city of Manaus

Jéssica de Souza Fortes (1); Valdete Santos de Araújo (2); Carla Souza Calheiros (3)

(1) Graduanda em Engenharia Civil, Universidade do Estado do Amazonas – UEA

(2, 3) Professora Doutora, Coordenação de Engenharia Civil – UEA

Avenida Darcy Vargas, 1200, Parque Dez – Manaus/AM. CEP 69065-020, Tel.: [phone]

Resumo

A ausência de controle tecnológico prejudica a produção de artefatos de meio-fio de qualidade. Visando o incentivo de pesquisas laboratoriais de artefatos de concreto sem função estrutural e a produção de um meio-fio que atinja à resistência mínima esperada de projeto, este estudo apresenta a análise das propriedades físicas e mecânicas e a durabilidade do concreto para a produção de meio-fio com cimento Portland e agregados oriundos da cidade de Manaus. Para tanto, foram realizados os ensaios de caracterização dos componentes do concreto, sendo eles, agregados naturais e reciclados: a areia natural, o seixo rolado e o Resíduo de Construção e Demolição (RCD), tido como uma alternativa sustentável e o cimento CP IV (Pozolânico). Foram feitos também ensaios com o concreto no seu estado fresco (slump test) e endurecido (análise macroscópica, resistência à compressão, absorção de água por imersão e carbonatação). O concreto produzido, por fim, obteve as seguintes resistências aos 28 dias de idade: Traço 1 (100% seixo – Referência) = 18,42 MPa; Traço 2 (100% seixo) = 17,27 MPa; Traço 3 (50% seixo + 50% RCD) = 18,27 MPa; e Traço 4 (100% RCD) = 17,09 MPa. Atingindo valores acima do estabelecido pela norma DNIT 020/2006 – ES do Departamento Nacional de Infraestrutura de Transportes (2006), porém não atendendo ao preconizado pelo Boletim Técnico 82 da Associação Brasileira de Cimento Portland (1997). Os valores de resistência dos Traços 2 e 4 poderiam ter sido superiores se houvesse o controle mais rigoroso quanto à relação água/cimento e ao adensamento do concreto. O Traço 3 apresenta os melhores resultados em relação ao traço de referência, tanto para o ensaio mecânico, quanto para os ensaios físicos e de durabilidade. Conclui-se que o concreto produzido através de dosagem experimental atinge resistências mínimas de projeto e, que o Resíduo de Construção e Demolição é uma alternativa ecologicamente viável do ponto de vista das propriedades físicas, mecânicas e de durabilidade do concreto; e do ponto de vista social-ambiental, ao atender o que preconiza a Resolução CONAMA 307 (2002), quanto à gestão de resíduos da construção civil.

Palavras-Chave: Artefato de concreto. Meio-fio. Dosagem. Durabilidade. Controle Tecnológico. RCD.

Abstract

The absence of technological control affects the production of quality curb artifacts. Aiming the incentive of laboratorial research of concrete artifacts with no structural function and the production of a curb that reaches the minimal resistance expected of the project, this study presents the analysis of the physical and mechanical properties and the durability of the concrete, to the production of curb made of Portland cement and aggregates coming of the city of Manaus. Therefore, were made tests for the characterization of the components of concrete, which are, natural and recycled aggregates: natural sand, pebble gravel and Construction and Demolition Waste (CDW), known as a sustainable alternative and the CP IV cement (Pozzolanic). Were made as well tests with the concrete in its fresh state (slump test) and hardened (macroscopic analysis, compressive strength, water absorption by immersion and carbonation). The concrete produced, ultimately, obtained these following resistances at 28 days of age: Mix 1 (100% boulder – reference) = 18.42 MPa; Mix 2 (100% boulder) = 17.27 MPa; Mix 3 (50% boulder + 50% CDW) =18.27 MPa; and, Mix 4 (100% CDW) = 17.09 MPa. Surpassing the value established by the norm DNIT 020/2006 – Service Specification (SS) of the National Department of Infrastructure and Transportation (2006), however the test doesn’t attend the Technical Bulletin 82 of the Brazilian Association of Portland Cement (1997). The resistance values of Mixes 2 and 4 could have been higher if the control were stricter in the water/cement ratio and the consolidation of concrete. The Mix 3 presents better results compared to the reference mix ratio in the mechanical, physical and durability tests. Concluding that the produced concrete by the experimental dosage reaches the project’s minimal resistance, and that the Construction and Demolition Waste is an environmentally viable alternative from the standpoint of physical, mechanical and durability of the concrete; and point of view social-environmental view, due attending the CONAMA 307 resolution (2002), addressing the management of construction waste.

Keywords: Concrete Artifact. Curb. Dosage. Durability. Technological Control. CDW.

1 Introdução

A microdrenagem é composta de diversos elementos que auxiliam o correto escoamento de águas superficiais, como, por exemplo, o meio-fio. Segundo a definição da Norma do Departamento Nacional de Infraestrutura de Transportes (DNIT 020/2006 – ES, 2006, p.2), o meio-fio é um limitador físico da plataforma rodoviária, que tem a função principal de “proteger o bordo da pista dos efeitos da erosão causada pelo escoamento das águas precipitadas sobre a plataforma”.

Pesquisas que utilizam artefatos de meio-fio como objeto de estudo são pouco difundidas na área de materiais de construção, portanto, ao se fazer o levantamento bibliográfico não se obteve êxito em relação aos trabalhos e estatísticas que trouxessem a qualidade dos artefatos de concreto de meio-fio pré-moldados no Brasil e/ou em Manaus. O fato é que o controle tecnológico destes artefatos por vezes não é feito pelas empresas que o fabricam. Assim, não há como garantir a qualidade dos mesmos. A falta do controle de qualidade pode ser observada principalmente quanto ao armazenamento do meio-fio, que fica exposto a intempéries e muitas vezes são utilizados da mesma forma que foram dispostos no local que serão empregados (Figura 1).

...